Crusher Backing Compound

Embrace the reliability of our Crusher Backing Compound, expertly engineered and supplied as a leading manufacturer, supplier, and exporter with over 14 years of unmatched experience in the field. Our trending product range, including Epoke Hi Impact 250 Crusher Backing Compound, Epoke Crusher Backing Compound, Cone Crusher Backing, and Mining Crusher Compound, stands out with its remarkable bond strength for supreme equipment protection, finest shock and vibration absorbance, excellent ease of application, superior chemical resistance, and extended machinery life. When compared to discount and generic alternatives, our crusher backing compounds offer personalized performance, trending technological advancements, and supreme durability, making them the prime choice in heavy-duty mining and quarry industries. Take advantage of our nationwide supply capability across All India to experience the finest and most reliable solution for all your crusher backing needs. Our commitment lies in delivering supreme quality, safety, and performance to ensure your business achieves its operational best.

Epoke Crusher Backing Compound

Epoke Crusher Backing Compound

MOQ : 50 Kilograms

Application
Backing of wear liners in cone & gyratory crushers

Application Method
Pouring/Casting

CAS No
25068-38-6

Color
Dark Grey

Color Retention
Excellent

Compressive Strength
>100 MPa

EINECS No
500-033-5

Hard dry time
24 hours

Product Type
Epoxy Based Crusher Backing Compound

Properties
Non-flammable, vibration and impact resistant, easy to mix and pour

Raw Material
Epoxy Resin & Hardener

Resistant Feature
High resistance to compression and abrasion

Service Period
Long term under normal operating conditions

Solid Content
100%

State
Liquid before curing

Thickness
As required (typically 10-20 mm)

Total dry time
18-24 hours

Touch Dry
6-8 hours

Cone Crusher Backing

Cone Crusher Backing

MOQ : 50 Kilograms

Application
Backing material for Cone Crushers and other heavy machinery, shock absorption, component support

Application Method
Pouring or trowelling

CAS No
25068-38-6

Color
Grey

Color Retention
Excellent

Compressive Strength
> 120 MPa

EINECS No
500-033-5

Hard dry time
24 hours

Product Type
Epoxy Crusher Backing Compound

Properties
High compressive strength, excellent adhesion, vibration damping, chemical resistance

Raw Material
Epoxy with Hardener

Resistant Feature
Resistant to oil, water, chemicals, and high-temperature cycling

Service Period
Long-term, dependent on operating conditions

Solid Content
99%

State
Two-component system (Resin and Hardener)

Thickness
Up to 10 mm per application

Total dry time
24 hours

Touch Dry
8-10 hours

Mining Crusher Compound

Mining Crusher Compound

MOQ : 50 Kilograms

Application
Mining Crusher Backing and Lining

Application Method
Pouring / Trowel

CAS No
9003-35-4

Color
Grey

Color Retention
Excellent

Compressive Strength
> 100 MPa

EINECS No
500-005-2

Hard dry time
24 hours

Product Type
Mining Crusher Compound

Properties
High Strength, Impact Resistant, Vibration Resistant

Raw Material
Epoxy Resin

Resistant Feature
Chemical and Wear Resistant

Service Period
2-3 years

Solid Content
100%

State
Paste

Thickness
3-10 mm

Total dry time
6 hours

Touch Dry
10-15 minutes

Epoke Hi Impact 250 Crusher Backing Compound

Epoke Hi Impact 250 Crusher Backing Compound

MOQ : 50 Kilograms

Application
Backing of Crusher liners and heavy equipment

Application Method
Pouring or trowelling

Color
Grey

Color Retention
Excellent

Compressive Strength
>100 MPa

Hard dry time
8-10 hours

Product Type
Crusher Backing Compound

Properties
High impact strength, excellent adhesion, vibration resistance

Raw Material
Epoxy Resin & Hardener Blend

Resistant Feature
Impact, Vibration, Chemical and Water Resistant

Service Period
12-24 months

Solid Content
100%

State
Liquid (Part A & B)

Thickness
10-12 mm

Total dry time
24 hours

Touch Dry
6-8 hours

✕